Australian alumina ban disrupts Rusal Ti6Al4V Powder prices for chemicals. Patel said. "One possible outcome could be Chinese buyers buying alumina and reselling it through eastern Russian ports." Rusal has a 20% stake in the Queensland Alumina Refinery, which has a capacity of 3.95 million tonnes a year, thus providing Rusal with 790,000 tonnes a year, Patel said. In addition, Rusal's Nikolaev refinery in Ukraine, which has an annual capacity of 1.75 million tonnes, has been suspended due to the conflict, he added. WoodMac said Rusal was also experiencing supply chain problems at its 2 million tonne a year Aughinish refinery in Ireland.
What is TC4(Ti6Al4V)?
TC4(Ti6Al4V) alloy is a medium strength α-β type two-phase titanium alloy containing 6% α-stabilizing element AI and 4% β-stabilizing element V. This alloy has excellent comprehensive properties and has obtained the most extensive applications in the aviation and aerospace industries. The long-term working temperature of the alloy can reach 400 ℃. In the aviation industry, it is mainly used to manufacture the fan and compressor disks and blades of the engine, as well as the important load-bearing components such as beams, joints and bulkheads in the aircraft structure.
The main semi-finished products of TC4 titanium alloy are bars, forgings, thick plates, thin plates, profiles and wires, etc. The alloy is mainly used in the annealed state, and can also be strengthened by solution aging treatment, but the hardened cross section is generally not more than 25mm.
The alloy has good process plasticity and superplasticity, and is suitable for various pressure forming. The alloy can also be welded and machined in various ways.
TC4(Ti6Al4V) heat treatment system
1. Annealing
Plate: 700-850℃, 0.5-2h, air cooling; bar and forging: 700-800℃, 1-2h, air cooling.
2. Vacuum annealing
700-800°C, 0.5-2h, the furnace is cooled to below 200°C to allow air cooling. The absolute pressure in the furnace should be no more than 0.09Pa.
3. Solution treatment
910-940℃, 0.5-2h, water quenching.
4. Aging
520-550°C, 2-4h, air cooling.
5. Stress relief annealing
Complete stress relief annealing: 600-650℃, 1-4h, air cooling; incomplete stress relief annealing: 500-600℃, 0.5-3h, air cooling. Stress relief annealing can be carried out in an air furnace or a vacuum furnace.
About KMPASS
KMPASS is a trusted global chemical material supplier & manufacturer with over 12 years experience in providing super high-quality chemicals and Nanomaterials. The company export to many countries, such as USA, Canada, Europe, UAE, South Africa, Tanzania,Kenya,Egypt,Nigeria,Cameroon,Uganda,Turkey,Mexico,Azerbaijan,Belgium,Cyprus,Czech Republic,Brazil, Chile, Argentina, Dubai, Japan, Korea, Vietnam, Thailand, Malaysia, Indonesia, Australia,Germany, France, Italy, Portugal etc. As a leading nanotechnology development manufacturer, KMPASS dominates the market. Our professional work team provides perfect solutions to help improve the efficiency of various industries, create value, and easily cope with various challenges. If you are looking for Ti6Al4V powder, please send an email to: sales2@nanotrun.com
The impact of the Russia-Ukraine conflict on the supply and prices of commodities is widening, and commodity prices remain at high levels. There is still great uncertainty about the future price of the Ti6Al4V Powder.
Inquery us
Roche and its subsidiary TIB Molbiol have developed a series of tests for the detection of the monkeypox virus, the Switzerland-based pharmaceutical company announced. The monkeypox virus is a close relative of the smallpox virus, belonging to orthp…
Early strength agent is an admixture which accelerates the development of concrete early strength and has no significant effect on later strength.…
Boron carbide (B4C) is an extremely hard boron-carbon ceramic and covalent material used in tank armor, bulletproof vests, engine damage powder, and many industrial applications.…